Butylated Urea Formaldehyde Resin
Acid Value: 2 max. mg KOH/g
Density: 1090 kg/m³
Viscosity at 25°C (Stokes): 15–30
Color (APHA): 100 max.
Solid Content: 60 ± 1%
Solvent: Isobutanol
This product offers good chemical resistance, fast curing, medium to high reactivity, good stability, and good compatibility/miscibility with short oil alkyd resins.
Isophthalic Unsaturated Polyester Resin
JSB-OUP 203-ST65 is a non-accelerated unsaturated polyester resin based on isophthalic acid / NPG. It has very low color, medium viscosity, low shrinkage, low water absorption, and very good mechanical properties. This resin is designed for curing at room temperature using methyl ethyl ketone peroxide (MEKP).
Appearance: Transparent
Color: 1 Gardner max. — ASTM D1544
Viscosity at 25°C: 800–1200 mPa·s / cP — ISO 2555
Density at 23°C: 1.12 ± 0.01 g/cm³ — ASTM D1475
Acid Value: 20 mg KOH/g max. — ASTM D1639
Solid Content: 66 ± 2% — ASTM D1259
Gel Time: 420–720 seconds — ASTM D2471
This product offers very low color, medium viscosity, low shrinkage and water absorption, good adhesion to glass fibers, hydrolysis resistance, and very good mechanical and chemical properties.
LONG OIL ALKYD RESIN BASED ON SOYA FATTY ACID
Oil Type: Soya Fatty Acid
Alcohol Type: Pentaerythritol
Oil Content: 62%
Acid Value: 10 max. mg KOH/g
Viscosity at 25°C (Stokes): 1800–2100
Color (Gardner): 4 max.
Solid Content: 70 ± 1%
Solvent: Mineral Spirit
This product offers excellent hardness, excellent surface and through drying, high gloss, excellent durability, good brushability, and good sagging resistance.
NON-PLASTICIZED BUTYLATED MELAMINE FORMALDEHYDE RESIN
Acid Value: 2 max. mg KOH/g
Density: 1090 kg/m³
Viscosity at 25°C (Stokes): 15–30
Color (APHA): 100 max.
Solid Content: 60 ± 1%
Solvent: Normal Butanol
This product offers excellent thermal and chemical resistance, fast curing, medium to high reactivity, suitable hardness,
Viscosity at 25°C (Stokes): 15–30
Color (APHA): 100 and good stability with short oil alkyd resins.